Factory supplied AISI 201 304 316 430 2b Ba No. 4/Hl Cold Rolled Mill Original Stainless Steel Sheet /Plate
With reliable quality process, good reputation and perfect customer service, the series of products produced by our company are exported to many countries and regions for Factory supplied AISI 201 304 316 430 2b Ba No. 4/Hl Cold Rolled Mill Original Stainless Steel Sheet /Plate, We sincerely do our greatest to supply the very best support for every one of the purchasers and businessmen.
With reliable quality process, good reputation and perfect customer service, the series of products produced by our company are exported to many countries and regions for China Stainless Steel Sheets 304 2b and AISI 304 Stainless Steel Sheet, For many years, we now have adhered to the principle of customer oriented, quality based, excellence pursuing, mutual benefit sharing. We hope, with great sincerity and good will, to have the honor to help with your further market.
AMS 4911 Titanium Alloy, Sheet, Strip, and Plate 6Al – 4V Annealed (Composition similar to UNS R56400)
1 .1 Form
This specification covers a titanium alloy in the form of sheet, strip, and plate up through 4.000 inches (101.60 mm) inclusive in thickness (See 8.5).
1 .2 Application
These products have been used typically for parts requiring strength up to 750 °F (399 °C), but usage is not limited to such applications.
1 .2.1 Certain processing procedures and service conditions may cause these products to become subject to stress-corrosion cracking; ARP982 recommends practices to minimize such conditions.
3.1 Composition
Shall conform to the percentages by weight shown in Table 1; carbon shall be determined in accordance with ASTM E1941, hydrogen in accordance with ASTM E1447, oxygen and nitrogen in accordance with ASTM E 1409, and other
elements in accordance with ASTM E539 or ASTM E2371. Other analytical methods may be used if acceptable to the purchaser.
3.3 Condition
The product shall be supplied in the following condition:
3.3.1 Sheet and Strip
Hot rolled with or without subsequent cold reduction, annealed, descaled, and leveled, having a surface appearance comparable to a commercial corrosion-resistant steel sheet No. 2D finish (See 8.2).
3.3.2 Plate
Hot rolled, annealed, descaled, and flattened, having a surface appearance comparable to commercial corrosion-
resistant steel No. 1 finish (See 8.2). Plate product shall be produced using standard industry practices for the production of the plate to the procured thickness. Bar, billet, forgings, or forging stock shall not be substituted for the plate.
3.4 Annealing
The product shall be annealed by heating to a temperature within the range 1 300 to 1 650 °F (704 to 899 °C), holding at the selected temperature within ±25 °F (±1 4 °C) for a time commensurate with product thickness and the heating equipment and procedure used, and cooling at a rate which will produce product meeting the requirements of 3.5. Pyrometry shall be in accordance with AMS2750.
3.5 Properties
The product shall conform to the following requirements and also shall meet the requirements of 3.5.1 and 3.5.2 after being reheated in air to 1325 °F ± 1 5 (718 °C ± 8), held at heat for 20 minutes ± 2, cooled at a rate equivalent to an air cool or slower.
3.5.1 Tensile Properties
Shall be as specified in Table 2, determined in accordance with ASTM E8 / E8M with the rate of strain set at
0.005 inch/inch/minute (0.005 mm/mm/minute) and maintained within a tolerance of ±0.002 inch/inch/minute
(0.002 mm/mm/minute) through the 0.2% offset yield strain.
3.5.2 Bending
Product under 0.1875 inch (4.762 mm) in nominal thickness shall have a test sample prepared nominally 0.750 inch(19.06 mm) in width, with its axis of bending parallel to the direction of rolling. The sample shall be bend tested in conformance with the guided bend test defined in ASTM E290 through an angle of 105 degrees. The test fixture supports shall have a contact radius 0.010 inch (0.25 mm) minimum, and the plunger shall have a radius equal to the bend factor shown in Table 3 times the nominal thickness. Examination of the bent sample shall not show evidence of cracking when examined at 1 5 to 25X magnification.
With reliable quality process, good reputation and perfect customer service, the series of products produced by our company are exported to many countries and regions for Factory supplied AISI 201 304 316 430 2b Ba No. 4/Hl Cold Rolled Mill Original Stainless Steel Sheet /Plate, We sincerely do our greatest to supply the very best support for every one of the purchasers and businessmen.
Factory supplied China Stainless Steel Sheets 304 2b and AISI 304 Stainless Steel Sheet, For many years, we now have adhered to the principle of customer oriented, quality based, excellence pursuing, mutual benefit sharing. We hope, with great sincerity and good will, to have the honor to help with your further market.